Select Page

Anode cap

An Anode cap is a shrinkable sleeve used to seal and protect a critical connection between the wire and the anode.

It helps with stress control at the anode exit and provides a watertight assembly as well as general electrical insulation. Ideal for protection against corrosion. It is the ideal solution to the problem of premature system failure due to corrosion causing lead wire to come out of the anode.

It is made of cross-linked Polyolefin with Mastic applied to the interior to ensure a watertight assembly in accordance with IP68.

TypeD-WireD-AnodeLengthLengthT
Before

shrink

After

shrink

Before

shrink

After

shrink

Total

TL

Anode

LA

Wire end

LW

Total

TL

Anode

LA

Wire end

LW

TATW
A4204120134,5120556514064763,52,5
A420A5020144,5115556013863753,52,5
A54082401651508070180100804,73,7
A540A108401651508565180100804,83,8
A550S1085020518090902601251354,74,9
A5501455020518095852601251354,74,9
Technical Specifications
FeaturesValuesStandard
Physical
Tensil strength:12N/mm² (MPA)(min)ASTM D638
Elongation:350 % (Min)ASTM D638
Density:1.1 gm/cm³ (Max)ASTM D792
Hardness:45 ± 10 Shore DASTM D2240
Water uptake:0.2 % (Max)ASTM D570
Corrosion:Non corrosiveASTM D2671
Thermal
Accelerated aging:(120ºC for 500 Hrs)ASTM D2671
Tensil strength:11 N/mm² (Mpa)(min)ASTM D638
Elongation:300 % (Min)ASTM D638
Low temperature flexibility:

(-40ºC for 4 Hours)

No crackingASTM D2671
Heat shock:No cracking or flowingESI 09-11
Shrink temperatur:125ºCIEC 216
Service temperature range:-55ºC to +1000CIEC 216
Electrical
Dielectric strength:12KV/mm. (Min)ASTM D149
Volume resistivity:1 x 10 Ohm.com(min)ASTM D257
Dielectric constant:5 (Max)ASTM D150